Steel Round Bars
High speed steel bar D3
high speed steel
D3
Dia Size: 2~200mm
RC Rockwell Hardness after
hardening and temper: 63-66
high speed steelD3Anneal temperature: 840-860oCRelief annealing temperature: 720-760oCHardening temperature: 1210-1240oCHardening medium: salt bath under 600oC,aslo use oil cooling or...
HSS Steel Bar M35
HSS with good performance, high hardness
BAR Round size:
diam: 2-200mm,length:1-6m.
produce cutting tools under high load
ALLOY STEEL H13Anneal temperature: 840-860oCRelief annealing temperature: 720-760oCHardening temperature: 1210-1230oCHardening medium:...
high speed steel bar SKH2(W18Cr4V)
HSS
good performance with high wear resistance
steel of tungsten
With the exclusive nature of hardeness,
redhardness
High speed steelSKH2(W18Cr4V)is a kind of high-speed steel of tungsten.With the exclusive nature of hardeness, redhardness and hot hardness.Spheroidizing...
High speed steel strips M35
M35
Steel flats size:
thinckness:0.8-3.0mm
width:8.0-12.0
HRC after hardening and temper:63-66
High speed steel M35Anneal temperature: 840-860oCRelief annealing temperature: 720-760oCHardening temperature: 1210-1230oCHardening medium: salt bath under 600oC,aslo use...
High speed steel bar W9(W9Mo3Cr4V)
high speed steel
W9Mo3Cr4V
Dia Size: 2~200mm
RC Rockwell Hardness after
hardening and temper: 63-66
high speed steel W9Mo3Cr4VAnneal temperature: 840-860oCRelief annealing temperature: 720-760oCHardening temperature: 1210-1240oCHardening medium: salt bath under...
Tool steel Cr12MoV
Tool steel Cr12MoV
Die steel SKD11(Cr12MoV)
Japanese cold forming die steel
Chinese grades:Cr12MoV
HRC great than 58
Tool steel Cr12MoVContent of elements %C:1.4~1.6 Si≤0.4 Mn≤0.6 Cr:11~13 Mo:0.5~1.2 V:0.2~0.5 S<=0.03 P<=0.03 Ni<0.5 Brinell...
High speed steel sheet W9(W9Mo3Cr4V)
high speed steel
W9Mo3Cr4V
Dia Size: 2~200mm
RC Rockwell Hardness after
hardening and temper: 63-66
high speed steel W9Mo3Cr4VAnneal temperature: 840-860oCRelief annealing temperature: 720-760oCHardening temperature: 1210-1240oCHardening medium: salt bath under...
HSS sheets\Din 1.3343\ Aisi M2\SKH9\SKH51\W6Mo5Cr4V2\6542
W6Mo5Cr4V2
Steel flats size:
thinckness:0.8-3.0mm
width:8.0-12.0
HRC:63-66 after hardening and temper
High speed steel flatsW6Mo5Cr4V2Anneal temperature: 840-860oCRelief annealing temperature: 720-760oCHardening temperature: 1210-1230oCHardening medium: salt bath...
High speed steel hot rolled bar W9(W9Mo3Cr4V)
high speed steel
W9Mo3Cr4V
Dia Size: 2~200mm
RC Rockwell Hardness after
hardening and temper: 63-66
high speed steel W9Mo3Cr4VAnneal temperature: 840-860oCRelief annealing temperature: 720-760oCHardening temperature: 1210-1240oCHardening medium: salt bath under...
High speed steel bar W9(W9Mo3Cr4V)
high speed steel
W9Mo3Cr4V
Dia Size: 2~200mm
RC Rockwell Hardness after
hardening and temper: 63H-66H
high speed steel W9Mo3Cr4VAnneal temperature: 840-860oCRelief annealing temperature: 720-760oCHardening temperature: 1210-1240oCHardening medium: salt bath under...